Experimental and Numerical Study of Mild Steel Behaviour under Cyclic Loading with Variable Strain Ranges

Table 5

Summary of experimental and numerical test results of steel specimens of grade S275 and S355.

Type	[GPa]	[MPa]	[MPa]		[%]	[%]	[%]
	Test	Test	Test	FEM		Test	Test
C_S275_01	206	334	459	454	1.09	9.88	—
C_S275_02	187	332	447	449	0.45	6.40	—
C_S275_03	195	279	453	447	1.32	6.38	—
C_S275_04	199	287	452	449	0.66	6.38	—
C_S275_05	195	322	459	443	3.49	6.73	—
C_S275_06	180	287	456	458	0.44	2.86	—
C_S275_07	218	289	459	453	1.31	8.10	33.67
C_S275_08	199	282	460	464	0.86	10.40	36.05
C_S275_09	207	284	458	460	0.44	9.41	35.03
C_S355_01	191	380	558	555	0.54	11.64	40.43
C_S355_02	190	384	559	558	0.18	3.61	29.20
C_S355_03	193	386	546	554	1.46	14.91	42.80
C_S355_04	192	379	563	560	0.53	17.61	47.62
C_S355_05	179	382	560	559	0.18	12.92	42.64
C_S355_06	185	386	563	564	0.18	13.97	43.82