Compositional Changes for Reduction of Polymerisation-Induced Shrinkage in Holographic Photopolymers
Table 4
Data from double exponential fit of relative shrinkage versus exposure time for BEA-doped AA photopolymer.
| Nanoparticle concentration (% wt.) | (%) | | (s) | | (s) |
| 0 | 3.40 ± 0.05 | 1.2 ± 0.1 | 9.50 ± 0.02 | 2.4 ± 0.1 | 62.50 ± 0.02 | 1 | 3.15 ± 0.04 | 1.2 ± 0.3 | 2.70 ± 0.09 | 2.69 ± 0.04 | 55.50 ± 0.01 | 2.5 | 2.94 ± 0.04 | 1.4 ± 0.5 | 2.2 ± 0.1 | 2.50 ± 0.04 | 50.00 ± 0.01 | 5 | 3.34 ± 0.05 | 0.9 ± 0.2 | 4.30 ± 0.08 | 2.70 ± 0.07 | 58.80 ± 0.01 |
|
|