Influence of Temperature on Typical Texture Distribution in Primary Recrystallization Matrix of 3% Si CGO Silicon Steel
Figure 5
Misorientation distribution under different intermediate annealing temperatures: (a) test group of samples intermediately annealed at 850°C; (b) test group of samples intermediately annealed at 820°C.