Off-Axial Tensile Properties of Precontraint PVDF Coated Polyester Fabrics under Different Tensile Rates
Table 2
Off-axial test results of Precontraint 702 T2 (100 mm/min).
| Angle | Tensile strength/(kN·m−1) | Strain at break/% | Average value | Standard deviation | Average value | Standard deviation |
| 0° | 58.051 | 3.444 | 13.541 | 0.154 | 5° | 50.542 | 1.633 | 12.662 | 0.061 | 15° | 44.834 | 0.864 | 18.072 | 0.760 | 25° | 39.271 | 1.664 | 32.556 | 0.363 | 35° | 38.081 | 1.827 | 38.992 | 0.338 | 45° | 37.709 | 0.733 | 40.416 | 0.189 | 55° | 37.981 | 0.198 | 39.101 | 0.348 | 65° | 40.771 | 0.908 | 32.662 | 0.144 | 75° | 45.934 | 0.945 | 21.441 | 0.201 | 85° | 51.339 | 2.345 | 14.100 | 0.126 | 90° | 58.699 | 0.966 | 14.446 | 0.125 |
|
|