Advances in Materials Science and Engineering / 2018 / Article / Fig 3

Research Article

Microstructural and Electrical Properties of Sn-Modified BaTiO3 Lead-Free Ceramics by Two-Step Sintering Method

Figure 3

The temperature dependence of dielectric permittivity of BTS ceramics sintered at different conditions at frequencies of 1, 10, and 100 kHz: (a) “1400/15/1000/6”; (b) “1400/30/1000/6”; (c) “1500/0/1000/6”; (d) “1500/15/1000/6”; (e) “1500/30/1000/6”; (f) loss factor (tanδ) of the BTS ceramics at 1 kHz.