Poole–Frenkel Emission Saturation and Its Effects on Time-to-Failure in Ta-Ta<sub>2</sub>O<sub>5</sub>-MnO<sub>2</sub> Capacitors

<div>PF emission saturation observed in 35 V 22 <i>μ</i>F chip tantalum capacitors. The <i>I</i>-<i>V</i> curve at −65°C converges with the curve at +25°C around 30 V and with the curve at +85°C near 35 V.</div>

Advances in Materials Science and Engineering

fig3

Figure 3

Figure 3: Poole–Frenkel Emission Saturation and Its Effects on Time-to-Failure in Ta-Ta<sub>2</sub>O<sub>5</sub>-MnO<sub>2</sub> Capacitors 

Advances in Materials Science and Engineering

Poole–Frenkel Emission Saturation and Its Effects on Time-to-Failure in Ta-Ta2O5-MnO2 Capacitors

Figure 3

Poole–Frenkel Emission Saturation and Its Effects on Time-to-Failure in Ta-Ta₂O₅-MnO₂ Capacitors