Hot Deformation Behavior and Microstructural Evolution of Twin-Roll-Casting Mg Alloy during High-Temperature Compression

<div>Microstructures of the twin-roll-cast (TRC) AZ31 alloy with different original sampling directions and different deformations at 500°C compression: (a) 0°-5%; (b) 5°-5%; (c) 10°-5%; (d) 0°-15%; (e) 5°-15%; (f) 10°-15%; (g) 0°-25%; (h) 5°-25%; (i) 10°-25%; (j) 0°-35%; (k) 5°-35%; (l) 10°-35%.</div>

Advances in Materials Science and Engineering

fig6

Figure 6

Figure 6: Hot Deformation Behavior and Microstructural Evolution of Twin-Roll-Casting Mg Alloy during High-Temperature Compression 