Three-Point Bending Fatigue Test of TiAl6V4 Titanium Alloy at Room Temperature
Table 2
Fatigue test results with used specimen numbering.
| Spec. no. | Number of cycles Nf | Mean stress σm (MPa) | Stress amplitude σa (MPa) | Maximum bending stress σO (MPa) | Notice |
| 1 | 2.0 × 107 | 613.0 | 287.0 | 901.0 | Polished, run-out | 2 | 1.8 × 107 | 389.0 | 1003.0 | Polished, break | 3 | 1.7 × 106 | 493.0 | 1107.0 | Polished, break | 4 | 1.6 × 105 | 552.0 | 1166.0 | Polished, break | 5 | 2.0 × 107 | 450.0 | 1064.0 | Polished, run-out | 6 | 1.2 × 106 | 477.0 | 1090.0 | Polished, break | 7 | 1.6 × 106 | 460.0 | 1074.0 | Polished, break | 8 | 2.0 × 107 | 454.0 | 1068.0 | Polished, run-out | 9 | 5.7 × 106 | 459.0 | 1073.0 | Polished, break | 10 | 1.2 × 107 | 455.0 | 1069.0 | Polished, break | 11 | 5.3 × 104 | 455.0 | 1068.0 | Non-polished, not included in S-N curve | 12 | 6.4 × 104 | 459.0 | 1073.0 | Non-polished, not included in S-N curve |
|
|