Analysis on Fracture Toughness of the L360QS/N08825 Bimetallic Composite Pipe Welded Joint
Table 3
CTOD values and parameters of specimens of L360QS/N08825 welded joint (20°C).
| Samples | Crack location | Mechanical properties | Thickness B (mm) | Width W (mm) | Crack length a0 (mm) | a0/W | CTOD value δm (mm) | Average value −δm (mm) |
| W1 | Weld | σs = 370 MPa | 19.82 | 39.88 | 21.55 | 0.54 | 1.2739 | 1.3232 | W2 | E = 2.1 × 105 MPa | 19.98 | 39.90 | 20.59 | 0.52 | 1.4935 | W3 | µ = 0.3 | 19.96 | 39.98 | 21.02 | 0.53 | 1.2022 |
| H1 | HAZ | σs = 370 MPa | 19.94 | 19.91 | 4.21 | 0.21 | 2.4457 | 1.5119 | H2 | E = 2.1 × 105 MPa | 19.96 | 19.94 | 3.36 | 0.17 | 0.9787 | H3 | µ = 0.3 | 19.92 | 19.85 | 3.77 | 0.19 | 1.1113 |
|
|