Table 1
Material properties and mismatch coefficient of welded joints.
| “Sandwich” material structure model | M | 0.7 | 0.8 | 0.9 | 1.0 | 1.1 | 1.2 | 1.3 | A508 | 476 | 476 | 476 | 476 | 476 | 476 | 476 | Alloy52 Mb | 333.6 | 393.0 | 428.4 | 476.0 | 523.6 | 571.2 | 618.8 |
| Continuous transition material model | Y (mm) | −5 ≤y ≤ 5 | σs (y) (MPa) | 14.24y + 404.8 | 8.3y + 434.5 | 4.76y + 452.2 | 476 | −4.76y + 499.8 | −8.3y + 523.6 | −14.24y + 547.4 | σs (MPa) | 333.6 ≤ σs ≤ 476 | 393 ≤σs ≤ 476 | 428.4 ≤ σs ≤ 476 | 476 | 523.6 ≤ σs ≤ 476 | 571.2 ≤ σs ≤ 476 | 618.8 ≤ σs ≤ 476 |
|
|