Selective Laser Melting of Diamond-Containing or Postnitrided Materials Intended for Impact-Abrasive Conditions: Experimental and Analytical Study
Table 1
Description of samples and SPS conditions.
| Sample | Printed lattice | Filling powder | SPS conditions: temperature, pressure, sintering time |
| No. 1 | 316L-5%wt. diamond | 316L | 900°C, 75 MPa, 14 min | No. 2 | 316L-10%wt. diamond | 316L | 900°C, 75 MPa, 14 min | No. 3 | TiN, 1.00 mm unit cell | Ti6Al4V | 900°C, 75 MPa, 14 min | No. 4 | TiN, 0.75 mm unit cell | Ti6Al4V | 900°C, 75 MPa, 14 min | No. 5 | Without lattice | 316L | 1000°C, 50 MPa, 10 min | No. 6 | Without lattice | Ti6Al4V | 1000°C, 50 MPa, 10 min |
|
|
5 and 6 are reference samples. |