The Effect of CuO on the Thermal Behavior of the High-Energy Combustion Agent of the Al/MnO2 System
Table 2
Gibbs free energy of five samples.
| Temperature (°C) | Absolute values of Gibbs free energy (kJ·mol−1) | Al + MnO2 | Al + MnO2 + CuO 5% | Al + MnO2 + CuO 10% | Al + MnO2 + CuO 15% | Al + MnO2 + CuO 20% |
| 0.000 | −956.591 | −948.912 | −939.981 | −931.104 | −921.698 | 100.000 | −952.489 | −944.908 | −936.079 | −927.303 | −917.996 | 200.000 | −948.061 | −940.571 | −931.840 | −923.159 | −913.944 | 300.000 | −943.503 | −936.095 | −927.454 | −918.860 | −909.728 | 400.000 | −938.927 | −931.592 | −923.030 | −914.513 | −905.454 | 500.000 | −934.364 | −927.091 | −918.600 | −910.150 | −901.152 | 600.000 | −929.790 | −922.568 | −914.139 | −905.747 | −896.801 | 700.000 | −924.202 | −917.046 | −908.693 | −900.373 | −891.493 | 800.000 | −917.477 | −910.389 | −902.118 | −893.874 | −885.064 | 900.000 | −910.807 | −903.778 | −895.578 | −887.401 | −878.650 | 1000.000 | −904.171 | −897.193 | −889.059 | −880.941 | −872.243 | 1100.000 | −897.603 | −890.686 | −882.628 | −874.580 | −865.946 | 1200.000 | −891.459 | −884.681 | −876.771 | −868.867 | −860.368 | 1300.000 | −886.249 | −879.240 | −871.124 | −863.002 | −854.278 | 1400.000 | −881.770 | −874.364 | −865.880 | −857.376 | −848.264 | 1500.000 | −877.380 | −869.561 | −860.697 | −851.796 | −842.280 |
|
|