Elliptical Method for Damage Identification in Carbon Fibre Reinforced Polymer Laminates
Table 1
Types of specimens and designations.
| Quantity | Designation | Material | Stacking sequence | Laminate type | Dimensions (mm) | Aspect ratio (a/b) |
| 2 | Plate A1–A3 | FibreDUX 6268C-HTA 12K | [90/±45/0]s | Quasi-isotropic | 310 × 240 × 2 | 1.29 | 2 | Plate B1-B2 | FibreDUX 6268C-HTA 12K | [90/0/±45]s | Quasi-isotropic | 310 × 240 × 2 | 1.29 | 2 | Plate C1–C3 | FibreDUX 6268C-HTA 12K | [90/0]2s | Cross-ply | 310 × 240 × 2 | 1.29 | 2 | Plate D1 | FibreDUX 6268C-HTA 12K | [902/03]s | Cross-ply | 310 × 240 × 2 | 1.29 | 1 | Plate E1 | FibreDUX 6268C-HTA 12K | [903/03]s | Cross-ply | 300 × 241 × 3 | 1.24 |
|
|