Recent Advances in Characterization Techniques for the Interface in Carbon Nanotube-Reinforced Polymer Nanocomposites
Table 2
Thermal resistance of the interface in carbon nanotube-reinforced polymer nanocomposites.
| Nanocomposites | Interfacial thermal resistance | Method | Reference |
| Carbon nanotube-octane | 3.3 × 10−8 m2·K/W | Simulation | [226] | Carbon nanotube-octane | 4.0 × 10−8 m2·K/W | Simulation | [227] | Carbon nanotube-EVA∗ | (0.2–9.6) × 10−8 m2·K/W | Simulation | [229] | Carbon nanotube-epoxy | (0.24–2.6) × 10−8 m2·K/W | Experimental | [230] | Carbon nanotube-epoxy | (0.77–2.5) × 10−8 m2·K/W | Simulation | [231] | Carbon nanotube-polyimide | 1.58 × 10−8 m2·K/W | Theoretical | [232] |
|
|
∗EVA: poly(ethylene vinyl acetate).
|