Features of Plasma Electrolytic Formation of Manganese- and Cobalt-Containing Composites on Aluminum Alloys
Table 2
The composition of aluminum alloys
, wt.%.
| Alloy grade | Al | Cu | Mg | Mn | Fe | Si | Zn | Ti | Other |
| A1050 | Min 99.5 | To 0.05 | To 0.05 | To 0.05 | To 0.4 | To 0.25 | To 0.07 | To 0.05 | To 0.03 | A2024 | 90.9–94.7 | 3.8–4.9 | 1.2–1.8 | 0.3–0.9 | ≤0.5 | ≤0.5 | ≤0.3 | ≤0.1 | Ni ≤ 0.1 | A3003 | 96.35–99.0 | ≤0.2 | ≤0.5 | 1.0–1.6 | ≤0.7 | ≤0.6 | ≤0.1 | — | — | AlSi12CuNiMg | 79.5–85.55 | 1.5–3.0 | 0.8–1.3 | 0.3–0.6 | ≤0.8 | 11.0–13.0 | ≤0.5 | ≤0.1 | Ni 0.8–1.3; Pb ≤ 0.1; Sn ≤ 0.02; Cr ≤ 0.2 |
|
|
Al, base of alloy; Al content is given approximately. |