Transformation of M/A Constituents during Tempering and Its Effects on Impact Toughness of Weld Metals for X80 Hot Bends
Figure 9
Inverse pole figures and boundary misorientation maps of the ferrite phase and phase distribution maps obtained from EBSD measurement of Bend C after tempering at different temperatures: (a)–(c) 550°C; (d)–(f) 620°C; (g)–(i) 680°C.