Structures, Morphological Control, and Antibacterial Performance of Ag/TiO2 Micro-Nanocomposite Materials
Table 3
Average diameters of micro-nanocomposite synthesized at each zone for all parameter settings.
| Baking time | Zone | Growth temperature | 800°C | 1000°C | 1200°C |
| 4 hours | 1 | 0.177 µm | 19.133 µm | 7.547 µm | 2 | 7.010 µm | 1.416 µm | 0.863 µm | 3 | 1.604 µm | 0.707 µm | 1.066 µm |
| 6 hours | 1 | 0.313 µm | 2.689 µm | 2.012 µm | 2 | 3.501 µm | 0.477 µm | 9.406 µm | 3 | 0.904 µm | 1.233 µm | 0.541 µm |
| 8 hours | 1 | 3.226 µm | 0.651 µm | 0.617 µm | 2 | 0.832 µm | 0.382 µm | 8.354 µm | 3 | 1.212 µm | 0.562 µm | 0.706 µm |
|
|