Optimization of Exothermic, Foaming, and Mechanical Properties of Modified Polyurethane as Filling Material for Goaf Sealing Wall
Table 7
Results of uniaxial compressive strength.
| No. | Factors | Index | | Polyether polyolsa : b | Catalyst A33 | Surfactant BL-8468 | UCS of PCS (MPa) | UCS of CCS (MPa) | UCS of CFS (MPa) |
| 1 | | 9 : 11 | 0.5 | 0.5 | 5.94 | 0.89 | 1.49 | 2 | | 9 : 11 | 0.8 | 0.6 | 3.26 | 0.18 | 1.31 | 3 | | 9 : 11 | 1.0 | 0.7 | 1.16 | 0.22 | 0.99 | 4 | | 9 : 11 | 1.2 | 0.8 | 3.37 | 0.16 | 1.63 | 5 | | 10 : 10 | 0.5 | 0.6 | 6.42 | 0.25 | 0.92 | 6 | | 10 : 10 | 0.8 | 0.5 | 3.74 | 0.39 | 0.58 | 7 | | 10 : 10 | 1.0 | 0.8 | 2.29 | 0.14 | 0.89 | 8 | | 10 : 10 | 1.2 | 0.7 | 2.19 | 0.44 | 0.65 | 9 | | 11 : 9 | 0.5 | 0.7 | 6.06 | 0.36 | 1.20 | 10 | | 11 : 9 | 0.8 | 0.8 | 4.90 | 0.21 | 1.48 | 11 | | 11 : 9 | 1.0 | 0.5 | 7.97 | 0.29 | 1.23 | 12 | | 11 : 9 | 1.2 | 0.6 | 5.98 | 0.44 | 0.99 | 13 | | 8 : 12 | 0.5 | 0.8 | 6.51 | 0.15 | 1.18 | 14 | | 8 : 12 | 0.8 | 0.7 | 8.45 | 0.13 | 1.42 | 15 | | 8 : 12 | 1.0 | 0.6 | 4.95 | 0.52 | 0.58 | 16 | | 8 : 12 | 1.2 | 0.5 | 2.93 | 0.21 | 0.83 |
| UCS of PCS | | 3.433 | 6.232 | 5.145 | | | | | 3.660 | 5.088 | 5.152 | | | | | 6.228 | 4.093 | 4.465 | | | | | 5.710 | 3.618 | 4.268 | | | | | 2.795 | 2.614 | 0.884 | | | |
| UCS of CCS | | 0.362 | 0.412 | 0.445 | | | | | 0.305 | 0.228 | 0.348 | | | | | 0.325 | 0.292 | 0.287 | | | | | 0.253 | 0.313 | 0.165 | | | | | 0.109 | 0.184 | 0.280 | | | |
| UCS of CFS | | 1.355 | 1.198 | 1.032 | | | | | 0.760 | 1.198 | 0.950 | | | | | 1.225 | 0.922 | 1.065 | | | | | 1.002 | 1.025 | 1.295 | | | | | 0.595 | 0.276 | 0.345 | | | |
|
|