Optimized Polynomial Virtual Fields Method for Constitutive Parameters Identification of Orthotropic Bimaterials
Table 1
Engineering elastic constants of orthotropic bimaterial.
| Exa (Mpa) | Eya (Mpa) | Eza (Mpa) | PRxya (Mpa) | PRyza (Mpa) | PRxza (Mpa) | Gxya (Mpa) | Gyza (Mpa) | Gxza (Mpa) |
| 180000 | 30000 | 8300 | 0.17 | 0.25 | 0.31 | 5700 | 12000 | 12000 |
| Exb (Mpa) | Eyb (Mpa) | Ezb (Mpa) | PRxyb (Mpa) | PRyzb (Mpa) | PRxzb (Mpa) | Gxyb (Mpa) | Gyzb (Mpa) | Gxzb (Mpa) |
| 175000 | 32000 | 8300 | 0.25 | 0.25 | 0.31 | 5700 | 12000 | 12000 |
|
|