Postprocessing Study for the Controllable Structures of Ceramic Green Parts Realized by a Flexible Binder Jetting Printing (BJP) Solution
Table 6
Comparison of final part performances between the integrated processing specimens in Groups VIII and IX and the corresponding reference specimens A and B postprocessed just by sintering.
Item for part performance
Specimen in group VIII1
Ref. specimen A
Specimen in group IX1
Ref. specimen B
Relative densities (%)
67.2 ± 1.22
66.4 ± 0.97
70.1 ± 1.15
67.8 ± 1.07
Flexural strength (MPa)
59.6 ± 1.81
59.9 ± 1.36
63.2 ± 1.79
62.6 ± 1.47
Compressive strength (MPa)
436.9 ± 21.33
431.6 ± 18.71
450.2 ± 20.11
435.3 ± 16.35
Surface roughness Ra (μm)
9.55 ± 0.43
16.73 ± 1.23
9.73 ± 0.56
16.01 ± 0.85
Vickers hardness (under 5 kgf, GPa)
4.47 ± 0.18
1.03 ± 0.29
4.58 ± 0.15
1.28 ± 0.39
1The specimens of Group VIII (IX) were infiltrated with 40 vol% slurry at 1 MPa pressure during the integrated postprocessing procedure.