Foaming Behavior and Pore Structure Evolution of Foamed Aluminum under the Extrusion Constraint
Table 3
The structure parameters of pores in samples at different furnace temperatures.
| Furnace temperature (°C) | Pipe A | Pipe B | 800 | 760 | 760 | 740 |
| Sample temperature, Ts (°C) | 710–750 | 710–750 | 710–750 | 710–750 | Porosity, P0 (%) | 72.4–78.7 | 69.8–76.1 | 69.5–74.4 | 71.0–75.1 | Average equivalent diameter, Da (mm) | 2.3–3.6 | 2.1–2.9 | 2.3–3.4 | 2.1–2.8 | Average circularity, Ca | 0.73–0.82 | 0.78–0.84 | 0.74–0.81 | 0.74–0.80 |
| Maximum expansion point | Temperature (°C) | 740 | 730 | 740 | 740 | Porosity, P0 (%) | 78.7 | 76.1 | 74.4 | 75.1 | Average equivalent diameter, Da (mm) | 3.6 | 2.7 | 2.6 | 2.5 | Average circularity, Ca | 0.73 | 0.81 | 0.78 | 0.76 |
|
|