Review Article
Reuse of Clay Brick Waste in Mortar and Concrete
| Chemical composition (%) | Reference | SiO2 | Al2O3 | Fe2O3 | CaO | SO3 | MgO | Na2O | K2O | TiO2 | MnO | P2O5 |
| 41.47 | 39.05 | 12.73 | 0.63 | 1.59 | — | — | 2.81 | 1.03 | — | — | [20] | 41.47 | 39.05 | 12.73 | 0.63 | 1.59 | — | — | 2.81 | 1.03 | — | — | [21] | 54.2 | 15.4 | 7.6 | 6.8 | 1.1 | 2.5 | — | — | — | — | — | [23] | 39.55 | 15.71 | 14.05 | 12.88 | 0.48 | 3.29 | — | 1.98 | — | — | — | [24] | 63.89 | 25.49 | 7.73 | 0.29 | — | 0.04 | Traces | 0.95 | — | — | — | [25] | 63.89 | 25.49 | 7.73 | 0.29 | — | 0.04 | Traces | 0.95 | Traces | Traces | — | [26] | 58.5 | 15.61 | 3.52 | 13.79 | 2.04 | 2.07 | 0.38 | 2.81 | 0.46 | 0.03 | 0.15 | [27] | 58.12 | 15.25 | 3.26 | 15.1 | 2 | 1.87 | 0.38 | 2.84 | 0.41 | 0.03 | 0.18 | | 58.34 | 15.14 | 3.22 | 14.1 | 2.02 | 2.22 | 0.39 | 2.82 | 0.49 | 0.04 | 0.17 | | 59.12 | 15.19 | 4.81 | 10.15 | 1.33 | 4.28 | 1.39 | 3.07 | 0.4 | 0.05 | 0.16 | | 58.13 | 15.24 | 4.63 | 10.57 | 1.42 | 4.32 | 1.42 | 3.08 | 0.39 | 0.05 | 0.16 | | 58.87 | 15.1 | 4.61 | 10.24 | 1.23 | 4.28 | 1.44 | 3.06 | 0.4 | 0.05 | 0.16 | | 77.43 | 9.27 | 3.9 | 2.89 | 0.11 | 1.36 | 0.8 | 2.26 | 0.62 | 0.06 | — | [28] | 73.83 | 12.94 | 5.52 | 1.67 | 0.12 | 1.36 | 0.9 | 2.18 | 0.84 | 0.08 | — | | 77.52 | 9.85 | 4.4 | 2.03 | 0.07 | 1.15 | 0.84 | 2.28 | 0.63 | 0.06 | — | | 72.83 | 12.01 | 5.73 | 2.95 | 0.09 | 1.7 | 0.99 | 1.94 | 0.72 | 0.09 | — | | 65.92 | 20.08 | 9.1 | 0.73 | — | 0.86 | 0.44 | 0.97 | 1.09 | — | — | [29] | 49.9 | 16.6 | 6.5 | 9.7 | 3.3 | 5.5 | 0.5 | 4.4 | 0.8 | 0.1 | 0.2 | [30] | 57.67 | 14.91 | 5.02 | 9.81 | 1.86 | 3.74 | 1.45 | 3.2 | — | — | — | [31] | 54.83 | 19.05 | 6 | 9.39 | 2.9 | 1.77 | 0.5 | 3.15 | 0.97 | — | 0.2 | [32] | 69.99 | 10.62 | 4.02 | 8.86 | 0.038 | 1.39 | 1.02 | 2.61 | 0.55 | — | 0.11 | | 68.79 | 15.23 | 6.28 | 1.79 | 0.127 | 2.02 | 0.26 | 3.71 | 0.85 | — | 0.07 | | 72.75 | 15.89 | 4.97 | 0.87 | 0.07 | 1.2 | 0.27 | 2.17 | 0.84 | — | 0.1 | | 67.58 | 18.94 | 8.084 | 0.948 | 0.13 | 0.719 | 0.246 | 1.884 | 1.06 | — | — | [33] | 69.26 | 14.17 | 6.3 | 4.28 | 0.02 | 2.25 | 0.28 | 1.34 | — | — | — | [34] | 53.8 | 14.1 | 12.1 | 9.2 | — | 8.9 | 1.3 | — | — | — | — | [35] | 69.43 | 17.29 | 6.4 | 0.51 | 2.54 | 1.14 | — | — | — | — | — | [36] | 67.9 | 15.2 | 5.1 | 0.6 | — | 1.2 | 0.8 | 1.5 | 0.8 | 0.1 | — | [37] | 75.06 | 14.25 | 5.61 | 1.3 | 0.7 | 1.35 | 0.19 | 0.08 | — | — | — | [38] | 52 | 40 | 1.5 | 0.5 | — | 0.3 | — | — | 5 | | | [39] | 50.91 | 15.29 | 8.97 | 12.7 | 0.2 | 4.06 | 0.83 | 0.76 | — | — | — | [40] |
|
|