Experimental Observation on the Pure Torsional Ratchetting of Polycarbonate Polymer at Room Temperature

<div>Curves of peak, valley, and ratchetting strains versus number of cycles obtained in stress-controlled cyclic tests at stress rete of 1 MPa/s and with various stress amplitude histories: (a) 35 ⟶ 25 ⟶ 35 MPa; (b) 25 ⟶ 35 ⟶ 25 MPa.</div>

Advances in Materials Science and Engineering

fig10

Figure 10

Figure 10: Experimental Observation on the Pure Torsional Ratchetting of Polycarbonate Polymer at Room Temperature 