Experimental Observation on the Pure Torsional Ratchetting of Polycarbonate Polymer at Room Temperature

<div>Curves of ratchetting strain versus number of cycles obtained in cyclic tests with various peak hold times and different stress levels, and at 1 MPa/s: (a) 35 ± 30 MPa; (b) 25 ± 30 MPa.</div>

Advances in Materials Science and Engineering

fig12

Figure 12

Figure 12: Experimental Observation on the Pure Torsional Ratchetting of Polycarbonate Polymer at Room Temperature 