Research Article
Experimental Observation on the Pure Torsional Ratchetting of Polycarbonate Polymer at Room Temperature
Figure 9
Curves of peak, valley, and ratchetting strains versus number of cycles obtained in stress-controlled cyclic tests at stress rate of 1 MPa/s and with various mean stress histories: (a) 35 ⟶ 25 ⟶ 35 MPa; (b) 25 ⟶ 35 ⟶ 25 MPa.
(a) |
(b) |