Through-Thickness Residual Stresses, Microstructure, and Mechanical Properties of Electron Beam-Welded CA6NM Martensitic Stainless Steel after Postweld Heat Treatment

<div>Microstructure of CA6NM in different regions of the EB welds (a) BM, (b) FZ, and (c) HAZ for the as-welded condition and (d) BM, (e) FZ, and (f) HAZ for the PWHTed condition.</div>