Through-Thickness Residual Stresses, Microstructure, and Mechanical Properties of Electron Beam-Welded CA6NM Martensitic Stainless Steel after Postweld Heat Treatment
Table 3
Global tensile properties and failure locations for CA6NM samples.
Sample
Direction
FZ/GL
Failure location
Regions in GL
YS (MPa)
UTS (MPa)
El (%)
Joint efficiency
L1–L6
Longitudinal to EB weld seam
1
FZ
FZ
721.6 ± 13.0
794.1 ± 1.5
22.2 ± 2.8
1.05
T1
Transverse to EB weld seam
0.9
FZ
FZ + HAZ
730.9
801.6
18.2 ± 1.1
1.06
T2
0.45
HAZ
FZ + HAZ
737.7
796.7
1.06
T3
0.35
BM
FZ + HAZ + BM
688.7
794.9
1.05
T4
0.2
BM
FZ + HAZ + BM
691.6
796.8
1.06
CA6NM [
12
]
N/A
N/A
N/A
N/A
550
755
15
N/A