Through-Thickness Residual Stresses, Microstructure, and Mechanical Properties of Electron Beam-Welded CA6NM Martensitic Stainless Steel after Postweld Heat Treatment

Table 4

Comparison of the tensile properties and failure locations for PWHTed CA6NM and UNS S41500.

Process	Material	Thickness (mm)	YS (MPa)	UTS (MPa)	El (%)	Failure location
EBW	CA6NM	90	691.6	796.8	18.2	BM
	UNS S41500 [21]	90	777.3	862.3	17.0
HLAW	CA6NM [31]	10	—	859.0	—	BM

FZ/GL ratio of 0.2 and GL consisting of BM, HAZ, and FZ.