Through-Thickness Residual Stresses, Microstructure, and Mechanical Properties of Electron Beam-Welded CA6NM Martensitic Stainless Steel after Postweld Heat Treatment
Table 5
YSL (MPa) for PWHTed CA6NM samples having different FZ/GL ratios.
| ||||||||||||||||||||||||||||||||||||||||||||||||
Region of strain localization and failure; region of peak hardness in HAZ close to FZ; HAZ just adjacent to BM. |