Measurement of Adhesion of In Situ Electrospun Nanofibers on Different Substrates by a Direct Pulling Method
Table 1
Experimental data collected from measurement of the adhesion force fa by using the home-made pulling system.
| Substrates | Voltage (kV) | h1 (cm) | (mm) | d1 (cm) | d2 (cm) | (N) | c (mm) | k | (N/cmā2) |
| Aluminium foil | 11 | 0.5 | 0.047 | 2.8 | 0.5 | 0.2298 | 15 | 0.4438 | 0.185166 | 12 | 0.5 | 0.035 | 1.5 | 0.5 | 0.2895 | 15 | 0.4438 | 0.196429 | 13 | 0.5 | 0.044 | 1.0 | 0.5 | 0.3021 | 15 | 0.4438 | 0.235372 |
| Virgin pulp paper | 11 | 0.5 | 0.062 | 2.0 | 1.0 | 0.8706 | 15 | 0.4438 | 0.014186 | 12 | 0.5 | 0.040 | 3.0 | 1.0 | 0.5754 | 15 | 0.4438 | 0.030572 | 13 | 0.5 | 0.062 | 4.4 | 1.0 | 0.4038 | 15 | 0.4438 | 0.030773 |
| Silicon paper | 11 | 0.5 | 0.096 | 5.4 | 1.0 | 0.0683 | 15 | 0.4438 | 0.007558 | 12 | 0.5 | 0.093 | 4.4 | 1.0 | 0.1579 | 15 | 0.4438 | 0.008561 | 13 | 0.5 | 0.091 | 3.9 | 1.0 | 0.0614 | 15 | 0.4438 | 0.013341 |
|
|