A Comparative Study on Structural, Morphological, and Tensile Properties of Binary and Ternary Epoxy Resin-Based Polymer Nanocomposites
Table 1
Mechanical property of epoxy-CaTiO3 NCPs.
| Strain at break (%) | Young’s modulus (MPa) | Force at break (N) | Elongation at break (mm) | Ultimate tensile strength (MPa) | CaTiO3 Content wt (%) | Fiberglass content wt. % |
| 4.444 | 2248.488 | 1701.7 | 2.222 | 47.564 | 1 | 0 | 3.340 | 2206.009 | 1598.0 | 1.670 | 42.207 | 3 | 0 | 2.949 | 2346.616 | 1778.3 | 1.474 | 46.274 | 5 | 0 | 3.246 | 2610.476 | 1893.5 | 1.623 | 49.271 | 7 | 0 | 3.348 | 2236.816 | 1742.7 | 1.674 | 45.42 | 1 | 0.1 | 3.586 | 2305.848 | 1776.6 | 1.793 | 46.41 | 3 | 0.1 | 2.454 | 2326.548 | 1610.6 | 1.227 | 41.91 | 5 | 0.1 | 2.442 | 2622.904 | 1612.7 | 1.221 | 41.97 | 7 | 0.1 | 3.811 | 1654.747 | 1139.3 | 1.906 | 30.52 | 1 | 0.2 | 2.816 | 2068.546 | 1572.4 | 1.408 | 40.91 | 3 | 0.2 | 1.228 | 2253.011 | 997.5 | 0.614 | 25.95 | 5 | 0.2 | 3.648 | 2300.663 | 1649.1 | 1.824 | 42.93 | 7 | 0.2 |
|
|