Study of Microstructure and Properties of 316L with Selective Laser Melting Based on Multivariate Interaction Influence
Table 4
Analysis of variance of surface roughness.
| Source | Sum of squares | DF | Mean square | F value | value prob > F |
| Model | 1172.94 | 27 | 43.44 | 10.47 | <0.0001 | A | 1.71 | 1 | 1.71 | 0.41 | 0.5263 | B | 1.153 10−3 | 1 | 1.153 10−3 | 2.778 10−4 | 0.9868 | C | 2.044 10−3 | 1 | 2.044 10−3 | 4.927 10−4 | 0.9825 | D | 119.63 | 1 | 119.63 | 28.83 | <0.0001 | E | 4.67 | 1 | 4.67 | 1.13 | 0.2983 | F | 767.11 | 1 | 767.11 | 184.88 | <0.0001 | AB | 1.02 | 1 | 1.02 | 0.24 | 0.6248 | AC | 17.07 | 1 | 17.07 | 4.11 | 0.0529 | AD | 0.13 | 1 | 0.13 | 0.031 | 0.8620 | AE | 0.11 | 1 | 0.11 | 0.027 | 0.8698 | AF | 0.19 | 1 | 0.19 | 0.045 | 0.8331 | BC | 2.00 | 1 | 2.00 | 0.48 | 0.4934 | BD | 0.53 | 1 | 0.53 | 0.13 | 0.7236 | BE | 3.59 | 1 | 3.59 | 0.86 | 0.3610 | BF | 0.49 | 1 | 0.49 | 0.12 | 0.7334 | CD | 7.34 | 1 | 7.34 | 1.77 | 0.1949 | CE | 0.84 | 1 | 0.84 | 0.20 | 0.6556 | CF | 1.12 | 1 | 1.12 | 0.27 | 0.6076 | DE | 0.22 | 1 | 0.22 | 0.052 | 0.8217 | DF | 91.57 | 1 | 91.57 | 22.07 | <0.0001 | EF | 16.06 | 1 | 16.06 | 3.87 | 0.0599 | Residual | 107.88 | 26 | 4.15 | | | Lack of fit | 97.78 | 21 | 4.66 | 2.31 | 0.1801 | Pure error | 10.10 | 5 | 2.02 | | | Cor total | 1280.82 | 53 | | | |
|
|