Study of Microstructure and Properties of 316L with Selective Laser Melting Based on Multivariate Interaction Influence
Table 5
Analysis of variance of density.
| Source | Sum of squares | DF | Mean square | F value | value prob > F |
| Model | 2035.96 | 27 | 75.41 | 8.30 | <0.0001 | A | 9.45 | 1 | 9.45 | 1.04 | 0.3171 | B | 77.01 | 1 | 77.01 | 8.48 | 0.0073 | C | 284.59 | 1 | 284.59 | 31.33 | <0.0001 | D | 617.80 | 1 | 617.80 | 68.01 | <0.0001 | E | 5.29 | 1 | 5.29 | 0.58 | 0.4524 | F | 193.92 | 1 | 193.92 | 21.35 | <0.0001 | AB | 2.46 | 1 | 2.46 | 0.27 | 0.6071 | AC | 124.75 | 1 | 124.75 | 13.73 | 0.0010 | AD | 36.18 | 1 | 36.18 | 3.98 | 0.0565 | AE | 9.62 | 1 | 9.62 | 1.06 | 0.3130 | AF | 10.56 | 1 | 10.56 | 1.16 | 0.2907 | BC | 22.97 | 1 | 22.97 | 2.53 | 0.1239 | BD | 75.91 | 1 | 75.91 | 8.36 | 0.0077 | BE | 10.67 | 1 | 10.67 | 1.17 | 0.2884 | BF | 8.24 | 1 | 8.24 | 0.91 | 0.3497 | CD | 40.77 | 1 | 40.77 | 4.49 | 0.0438 | CE | 1.84 | 1 | 1.84 | 0.20 | 0.6560 | CF | 1.00 | 1 | 1.00 | 0.11 | 0.7425 | DE | 166.10 | 1 | 166.10 | 18.29 | 0.0002 | DF | 73.58 | 1 | 73.58 | 8.10 | 0.0085 | EF | 56.59 | 1 | 56.59 | 6.23 | 0.0192 | Residual | 236.18 | 26 | 9.08 | | | Lack of fit | 167.32 | 21 | 7.97 | 0.58 | 0.8281 | Pure error | 68.86 | 5 | 13.77 | | | Cor total | 2272.13 | 53 | | | |
|
|