Study of Microstructure and Properties of 316L with Selective Laser Melting Based on Multivariate Interaction Influence
Table 6
Analysis of variance of tensile strength.
| Source | Sum of squares | DF | Mean square | F value | value prob > F |
| Model | 1.227 106 | 27 | 45454.48 | 14.31 | <0.0001 | A | 30861.77 | 1 | 30861.77 | 9.72 | 0.0044 | B | 44371.38 | 1 | 44371.38 | 13.97 | 0.0009 | C | 8444.14 | 1 | 8444.14 | 2.66 | 0.1150 | D | 6.023 105 | 1 | 6.023 105 | 189.67 | <0.0001 | E | 686.54 | 1 | 686.54 | 0.22 | 0.6458 | F | 50015.45 | 1 | 50015.45 | 15.75 | 0.0005 | AB | 0.16 | 1 | 0.16 | 4.947 10−5 | 0.9944 | AC | 4936.40 | 1 | 4936.40 | 1.55 | 0.2236 | AD | 25955.86 | 1 | 25955.86 | 8.17 | 0.0083 | AE | 3.46 | 1 | 3.46 | 1.089 10−3 | 0.9739 | AF | 5545.85 | 1 | 5545.85 | 1.75 | 0.1978 | BC | 2596.73 | 1 | 2596.73 | 0.82 | 0.3741 | BD | 22248.05 | 1 | 22248.05 | 7.01 | 0.0136 | BE | 5530.04 | 1 | 5530.04 | 1.74 | 0.1985 | BF | 7718.38 | 1 | 7718.38 | 2.43 | 0.1311 | CD | 577.70 | 1 | 577.70 | 0.18 | 0.6732 | CE | 686.80 | 1 | 686.80 | 0.22 | 0.6458 | CF | 594.23 | 1 | 594.23 | 0.19 | 0.6689 | DE | 2029.53 | 1 | 2029.53 | 0.64 | 0.4313 | DF | 113.57 | 1 | 113.57 | 0.036 | 0.8515 | EF | 11412.79 | 1 | 11412.79 | 3.59 | 0.0692 | Residual | 82562.08 | 26 | 3175.46 | | | Lack of fit | 77877.06 | 21 | 3708.43 | 3.96 | 0.0663 | Pure error | 4685.02 | 5 | 937.00 | | | Cor total | 1.310 106 | 53 | | | |
|
|