Study of Microstructure and Properties of 316L with Selective Laser Melting Based on Multivariate Interaction Influence
Table 7
Analysis of variance of elongation.
| Source | Sum of squares | DF | Mean square | F value | value prob > F |
| Model | 10386.66 | 27 | 384.69 | 14.05 | <0.0001 | A | 350.33 | 1 | 350.33 | 12.80 | 0.0014 | B | 138.03 | 1 | 138.03 | 5.04 | 0.0335 | C | 89.58 | 1 | 89.58 | 3.27 | 0.0820 | D | 4864.16 | 1 | 4864.16 | 177.70 | <0.0001 | E | 1.30 | 1 | 1.30 | 0.048 | 0.8289 | F | 58.73 | 1 | 58.73 | 2.15 | 0.1550 | AB | 333.82 | 1 | 333.82 | 12.20 | 0.0017 | AC | 34.91 | 1 | 34.91 | 1.28 | 0.2691 | AD | 51.06 | 1 | 51.06 | 1.87 | 0.1837 | AE | 336.05 | 1 | 336.05 | 12.28 | 0.0017 | AF | 49.00 | 1 | 49.00 | 1.79 | 0.1925 | BC | 0.076 | 1 | 0.076 | 2.762 10−3 | 0.9585 | BD | 195.25 | 1 | 195.25 | 7.13 | 0.0129 | BE | 39.24 | 1 | 39.24 | 1.43 | 0.2420 | BF | 4.86 | 1 | 4.86 | 0.18 | 0.6771 | CD | 3.90 | 1 | 3.90 | 0.14 | 0.7087 | CE | 1.58 | 1 | 1.58 | 0.058 | 0.8120 | CF | 0.16 | 1 | 0.16 | 5.684 10−3 | 0.9405 | DE | 107.43 | 1 | 107.43 | 3.92 | 0.0582 | DF | 325.69 | 1 | 325.69 | 11.90 | 0.0019 | EF | 14.25 | 1 | 14.25 | 0.52 | 0.4770 | Residual | 711.70 | 26 | 27.37 | | | Lack of fit | 670.62 | 21 | 31.93 | 3.89 | 0.0687 | Pure error | 41.08 | 5 | 8.22 | | | Cor total | 11098.36 | 53 | | | |
|
|