Multiobjective Optimization of Milling Parameters for Ultrahigh-Strength Steel AF1410 Based on the NSGA-II Method
Table 7
Results of NSGA-II (only first 30 solutions were taken).
| Number of tests | Process parameter | Milling force Ft (N) | Surface roughness Ra (μm) | Material removal rate MRR (mm3/min) | (m/min) | fz (mm/z) | ap (mm) | ae (mm) |
| 1 | 25.12 | 0.06 | 5.00 | 2.00 | 455.32 | 0.352 | 1919 | 2 | 17.25 | 0.03 | 1.00 | 0.50 | 59.10 | 0.264 | 32 | 3 | 25.12 | 0.02 | 5.00 | 0.50 | 123.86 | 0.147 | 188 | 4 | 16.63 | 0.02 | 1.00 | 0.50 | 61.79 | 0.258 | 21 | 5 | 25.12 | 0.06 | 5.00 | 2.00 | 455.32 | 0.352 | 1919 | 6 | 25.12 | 0.06 | 5.00 | 1.96 | 451.13 | 0.352 | 1882 | 7 | 25.12 | 0.06 | 5.00 | 1.18 | 328.63 | 0.305 | 1101 | 8 | 25.12 | 0.06 | 5.00 | 1.15 | 315.81 | 0.295 | 1034 | 9 | 25.12 | 0.06 | 5.00 | 0.56 | 190.92 | 0.198 | 505 | 10 | 25.11 | 0.05 | 5.00 | 0.60 | 196.72 | 0.203 | 528 | 11 | 24.49 | 0.06 | 1.00 | 0.73 | 121.85 | 0.296 | 135 | 12 | 25.12 | 0.03 | 5.00 | 0.50 | 126.05 | 0.148 | 209 | 13 | 25.12 | 0.05 | 5.00 | 0.65 | 206.82 | 0.212 | 566 | 14 | 25.12 | 0.06 | 4.97 | 1.02 | 297.79 | 0.283 | 941 | 15 | 25.12 | 0.03 | 5.00 | 0.50 | 129.29 | 0.149 | 245 | 16 | 25.11 | 0.05 | 4.99 | 2.00 | 430.78 | 0.333 | 1741 | 17 | 24.48 | 0.04 | 1.15 | 0.57 | 86.28 | 0.251 | 80 | 18 | 25.09 | 0.06 | 5.00 | 1.52 | 392.49 | 0.341 | 1457 | 19 | 25.12 | 0.06 | 5.00 | 0.95 | 278.76 | 0.270 | 863 | 20 | 25.12 | 0.05 | 5.00 | 0.64 | 204.38 | 0.210 | 557 | 21 | 25.12 | 0.04 | 5.00 | 0.50 | 136.58 | 0.153 | 294 | 22 | 25.12 | 0.06 | 5.00 | 0.81 | 256.17 | 0.253 | 764 | 23 | 25.12 | 0.06 | 5.00 | 0.93 | 275.79 | 0.267 | 850 | 24 | 25.12 | 0.06 | 5.00 | 0.96 | 281.36 | 0.272 | 875 | 25 | 25.12 | 0.06 | 5.00 | 0.53 | 181.75 | 0.190 | 472 | 26 | 25.12 | 0.06 | 5.00 | 0.94 | 283.35 | 0.274 | 884 | 27 | 25.12 | 0.06 | 5.00 | 0.75 | 233.95 | 0.234 | 673 | 28 | 25.12 | 0.06 | 5.00 | 1.35 | 349.01 | 0.314 | 1204 | 29 | 24.60 | 0.06 | 1.00 | 0.56 | 95.74 | 0.275 | 103 | 30 | 25.09 | 0.06 | 5.00 | 1.49 | 381.39 | 0.334 | 1390 |
|
|